Ruger Old Army pitting

R

richfr

New member
I have a Ruger Old Army that has a fair amount of pitting on the frame and barrel (outside only) it was like this when I got it. I got them as a pair as the other one was perfect.
I thought it was made of stainless steel due to the colour and shine but have been informed it may just be a steel one that has been polished as stainless doesn’t corrode in this way.
The serial number is 145-267** which as far as I can tell means it’s a stainless one :confused:
Can anybody confirm stainless can have damage like this?
 
Absolutely. Pitting is the way that stainless steel "rusts". My materials science buddy in the next office says that it happens when the passivation is compromised in a small area, causing it to become an anode, while the rest of the metal is a cathode. Then you get galvanic corrosion right around that spot, causing a pit.

He went on and on about ionic migration, half-reactions and electromigration, but I stopped him pretty quick.

He also mentioned that that's why steel that's been blued or parkerized tends to get pits. The bluing or parkerization is a passivation layer and when it gets compromised, that particular spot corrodes just like your revolver did.
 
Stainless corrodes when abused, and black powder well just accelerate it. The benefit of stainless is this damage can often be cleaned up. Depending on how deep the pitting is you may be able to sand and polish this revolver to a near new looking condition.

My stainless ROA came cheap because of it's surface imperfections. Careful sanding of the pitted areas and then buffed on a 10" buffing wheel made a big difference in appearance.

ROA01.jpg
 
The stainless that the Ruger Old Army is made of doesn't seem to be very rust resistant.
Perhaps Ruger uses it more for its strength.
 
robhof

I've got some pitting in the barrel a SS ROA that I recently picked up. The outside was fairly good, but it appears that a previous owner had a squib and waited a time before removing it. There's a ring of pitting about 1" in from the end of the bore, the good news is that it still shoots as well as my NIB original that I got years ago.
 
Well thanks madcratebuilder I decided to give it a go and ordered a bench grinder polishing kit. It is going to take some time to get it how I want it but I got most of the pitting out with a little sanding. Just need to wet and dry it then get to work polising :D
Here are some before pics :o

IMG_5788.jpg


IMG_5785.jpg


IMG_5787.jpg


IMG_5794.jpg


There are marks in difficult to get at places and a little on the warning on the top but I think I can get it back to a fair standard with more elbow grease.
I will put some pics up when I am done.
I think I will get a new front sight and a SS bolt kit for it too.
Anybody know of a good retailer that stocks these parts that might ship to France?

Thanks
 
Was this revolver possibly shot with a substitute powder instead of real black powder? Some of those products contain chlorates and are more corrosive than black powder.
 
I have no idea what happened to it but the cylinder and barrel inside are good so it’s not that it was left dirty.
I got a pair of them from a guy that was giving up shooting he said he bought them like that.
The other one is almost perfect and will be 100% after a quick buff up. I plan on keeping the better one and selling this on to fund some casting equipment.
 
My guess is it was left for some time in a leather holster. They might have cleaned it and then put it back in the holster.

I have a Ruger Old Army that I bought new when they were first available. It still looks new. When I'm finished shooting (usually Pyrodex) I remove the grips and drop the whole gun in a pan of warm soapy water and let is soak for at least an hour, scrub it clean, blow it off with an air hose, set the oven on 150 and bake it for 20 minutes or so. You wouldn't want to set the oven temp any higher as that could weaken some parts but it will drive any moisture out of the action. Lube it while it's still warm.
 
Here are some pics after some hard work sanding and polishing. Am very happy with the results :D it’s not perfect but a huge improvement and you now have to look very close to see any marks.

IMG_5899.jpg


IMG_5886.jpg


IMG_5885.jpg
 
You must log in or register to reply here.