for my purposes they would be pistol calibers fired from either handguns or carbines.
mostly it would just be plinking, but depending on accuracy, weight retention and expansion wouldn't mind for medium game hunting.
I suppose more pointed questions would get better results. between the three (at velocities below 1600FPS):
1. does any one of them prevent lead fowling better than the others?
2. does any one of them leave garbage behind in your barrel?
3. do any of them affect weight retention/expansion beyond what is already affected by alloy composition and bullet construction?
to T.O'Heir- I'm well aware that it's not a Jacket, that's why there's quotations around "cheap jacket". that's why I'm asking about these three specifically, and not about jacket thickness, bullet construction, and bonding processes.