au contraire......It’s not going to allow you to run soft lead bullets at rifle velocities.
If I am not mistaken, air cooling results in annealing (softening), bullets as it would with heat treating Carbon Steel. You have to quench to get the hardness.Specifically the 400°f bake cycles, which seems very close to what you would do to air-cool or water quench for increasing hardness.